高溶解性树枝状富勒烯衍生物电子传输材料的合成及其在钙钛矿太阳能电池中的应用

作     者：程政淳 方引于 王艾菲 马涛涛 刘芳 高松 严苏豪 狄毅 秦天石 CHENG Zheng-chun;FANG Yin-yu;WANG Ai-fei;MA Tao-tao;LIU Fang;GAO Song;YAN Su-hao;DI Yi;QIN Tian-shi

作者机构：Institute of Advanced Materials(IAM)Nanjing Tech UniversityNanjing 210009China Ningbo Institute of Northwestern Polytechnical UniversityNingbo 315103China Shaanxi Institute of Flexible ElectronicsNorthwestern Polytechnical UniversityXi'an 710072China 

基　　金：Projects(2017YFE0131900,2017YFB0404500)supported by National Key Research and Development Program of China Projects(91833306,91733302,62075094)supported by the National Natural Science Foundation of China Project(202003N4004)supported by the Ningbo Natural Science Foundation,China Project(2020GXLH-Z-014)supported by the Joint Research Funds of Department of Science&Technology of Shaanxi Province and Northwestern Polytechnical University,China 

出 版 物：《Journal of Central South University》 (中南大学学报（英文版）)

年 卷 期：2021年第28卷第12期

页      码：3714-3727页

摘      要：本文设计并合成了一系列单加成的树枝状C_(60)衍生物作为电子传输材料,其中,材料的合成过程采用无催化剂参与的Diels-Alder[4+2]环加成反应。得到的超支化C_(60)的溶解性得到明显提高,与原始的C_(60)相比,第一代和第二代树枝状C_(60)衍生物(C_(60)-G1和C_(60)-G2)在有机相中的溶解度均提高了5倍以上。此外,理论模拟和实验均表明,树枝状C_(60)衍生物可作为钙钛矿太阳能电池的电子传输层,并同时具有良好的溶液加工性能。在钙钛矿太阳能电池中,以C_(60)-G2作为电子传输层的最大光电转换效率可达14.7%。

主 题 词：树枝状聚合物 C_(60)富勒烯 电子传输材料 提高溶解度 钙钛矿太阳能电池 

学科分类：0806[工学-电气类] 08[工学] 080501[080501] 0805[工学-能源动力学] 080502[080502] 

核心收录：

D　O　I：10.1007/s11771-021-4885-5

馆 藏 号：203107125...