相溶解协同提升高熵合金的强度和塑性

作     者：王睿鑫 李理 唐宇 雷智锋 李甲 马超 李顺 叶益聪 朱利安 艾园林 方棋洪 白书欣 吕昭平 Ruixin Wang;Li Li;Yu Tang;Zhifeng Lei;Jia Li;Chao Ma;Shun Li;Yicong Ye;Li'an Zhu;Yuanlin Ai;Qihong Fang;Shuxin Bai;Zhaoping Lu

作者机构：College of Aerospace Science and EngineeringNational University of Defense TechnologyChangsha 410073China State Key Laboratory of Advanced Design and Manufacturing for Vehicle BodyHunan UniversityChangsha 410082China College of Materials Science and EngineeringHunan UniversityChangsha 410082China State Key Laboratory for Advanced Metals and MaterialsUniversity of Science and Technology BeijingBeijing 100083China Department of Mechanics and Engineering ScienceCollege of EngineeringPeking UniversityBeijing 100871China 

基　　金：supported by the National Natural Science Foundation of China(52171166,52101194,11972372 and U20A20231) the Fundamental Research Funds for the Central Universities(531118010621) the Postgraduate Scientific Research Innovation Project of Hunan Province(CX20210076) 

出 版 物：《Science China Materials》 (中国科学（材料科学（英文版）)

年 卷 期：2023年第66卷第3期

页      码：1205-1214页

摘      要：热处理是金属材料热机械加工的常用手段.随着热处理温度的升高而湮灭的缺陷通常导致材料的塑性提升而强度降低.本研究中,我们通过提高热处理温度促进相溶解而协同提升了TiZrNbTa高熵合金的强度和塑性.当热处理温度从800提升至1250°C,合金的拉伸屈服强度提高了40%,达到1003±16 MPa.同时,合金的伸长率增加了近一倍,达到16.79%±1.03%.热处理温度提升引起的相溶解加剧了晶格畸变,从而增强了晶格摩擦应力并提升了屈服强度.相溶解也降低了界面失配并缓解了应力集中.此外,1250°C热处理合金中的局部化学有序结构促进了位错共平面滑移和位错增殖.两种机制共同提升了合金的塑性.该研究不仅扩展了关于金属材料中热处理和相溶解的理解,而且也为合金的强韧化设计提供了思路.

主 题 词：金属材料 热机械加工 平面滑移 高熵合金 拉伸屈服强度 摩擦应力 晶格畸变 应力集中 

学科分类：08[工学] 080502[080502] 0805[工学-能源动力学] 

核心收录：

D　O　I：10.1007/s40843-022-2254-8