ZIF-67基纳米多孔衍生碳的制备及其电容去离子性能研究

作     者：张龙玉 王锐 柴文翠 马梦瑶 李林科 ZHANG Long-yu;WANG Rui;CHAI Wen-cui;MA Meng-yao;LI Lin-ke

作者机构：College of ChemistryZhengzhou UniversityZhengzhou 450001China Henan Laboratory of Critical MetalsZhengzhou UniversityZhengzhou 450001China School of Chemical EngineeringZhengzhou UniversityZhengzhou 450001China 

基　　金：Project(22180012)supported by the High-level Talent Introduction and Training Project of Zhengzhou University,China Project(21A610011)supported by the Key Scientific Research Projects of Colleges and Universities in Henan Province,China Projects(92061201,21825106,22001236)supported by the National Natural Science Foundation of China Project(9IRTSTHN022)supported by the Program for Innovative Research Team(in Science and Technology)in Universities of Henan Province and Zhengzhou University,China 

出 版 物：《中南大学学报:英文版》 (Journal of Central South University)

年 卷 期：2023年第30卷第8期

页      码：2485-2500页

摘      要：电容去离子(CDI)是一种具有良好发展前景的脱盐技术,CDI脱盐性能很大程度上取决于电极材料的结构和性质。本文以金属有机框架材料ZIF-67作为前驱体,制备了三种不同形态结构的ZIF-67基纳米多孔衍生碳材料,包括碳纳米盒(ZCNB)、碳纳米管(ZCNT)以及碳纳米盒和碳纳米管混合物(ZCNH),并研究了三种衍生碳材料的孔隙结构、表面性质、电化学性质与CDI性能构效关系。结果表明,三种ZIF-67基纳米多孔衍生碳材料中,由于ZCNB具有高比表面积、良好的润湿性、高表面电荷和合适的孔径,因此ZCNB具有最高的CDI除盐能力。尽管ZCNH和ZCNT中的碳纳米管可以提高碳材料的导电性,但同时降低了碳材料的比表面积和表面润湿性,从而降低了CDI除盐性能。本文将为MOFs基衍生碳电极材料的设计提供理论和实验指导。

主 题 词：多孔碳 金属有机框架材料 ZIF-67 电容去离子 

学科分类：081702[081702] 08[工学] 0817[工学-轻工类] 0805[工学-能源动力学] 0703[理学-化学类] 

核心收录：

D　O　I：10.1007/s11771-023-5394-5

馆 藏 号：203124050...