挤压态Mg-5.25wt.%Zn-0.6wt.%Ca可降解镁合金的体内外研究（英文）

作     者：顾雪楠 王凡 谢鑫荟 郑明毅 李萍 郑玉峰 秦岭 樊瑜波 Xuenan Gu;Fan Wang;Xinhui Xie;Mingyi Zheng;Ping Li;Yufeng Zheng;Ling Qin;Yubo Fan

作者机构：School of Biological Science and Medical EngineeringBeihang UniversityBeijing 100083China Beijing Advanced Innovation Centre for Biomedical EngineeringBeihang UniversityBeijing 102402China Department of Orthopaedics and TraumatologyThe Chinese University of Hong KongHong KongChina School of Materials science and EngineeringHarbin Institute of TechnologyHarbin 150001China Department of Materials Science and EngineeringCollege of EngineeringPeking UniversityBeijing 100871China National Research Center for Rehabilitation Technical AidsBeijing 100176China 

基　　金：supported by the National Natural Science Foundation of China(51401007,11472032,11120101001 and 11421202) a foundation for the author of the National Excellent Doctoral Dissertation of China(201463) Young Elite Scientists Sponsorship Program By CAST(2017QNRC001) the National Key Research and Development Plan(2016YFC1102203 and 2016YFC1101100) 

出 版 物：《Science China Materials》 (中国科学（材料科学（英文版）)

年 卷 期：2018年第61卷第4期

页      码：619-628页

摘      要：可降解医用镁合金在骨科领域显示出良好的应用前景.为了保证镁合金的生物相容性,本文设计了全营养元素组成的Mg-Zn-Ca合金,研究了其体内外腐蚀及生物相容性.Mg-Zn-Ca合金在五种模拟体液中的腐蚀测试结果表明在Hank’s和MEM中添加血清能够降低合金腐蚀速度,并提高腐蚀均匀性.血清浓度越高,合金腐蚀速率越低.Mg-Zn-Ca合金在MEM+10%FBS溶液中腐蚀速率低,腐蚀形貌均匀.直接法和间接法的细胞实验结果均显示Mg-Zn-Ca合金具有良好的细胞相容性.动物实验结果表明,Mg-Zn-Ca合金在小鼠骨髓腔内逐步降解,4周后残余40 vol.%.micro-CT和组织学观察显示植入体周围有新骨形成,且随着植入时间延长,皮质骨厚度增加.因此,挤压态Mg-Zn-Ca合金具有良好的生物相容性,有望用作骨科植入材料,但是其体内降解速率还应进一步降低.

主 题 词：镁合金 可降解 体内 生物相容性 细胞相容性 腐蚀速度 血清浓度 腐蚀速率 