原位构筑表面缺陷的碳掺杂型三元钴镍铁磷化物纳米立方体用于高效全水分解（英文）

作     者：高文坤 杨敏 迟京起 张鑫宇 谢静宜 郭宝玉 王磊 柴永明 董斌 Wen-Kun Gao;Min Yang;Jing-Qi Chi;Xin-Yu Zhang;Jing-Yi Xie;Bao-Yu Guo;Lei Wang;Yong-Ming Chai;Bin Dong

作者机构：State Key Laboratory of Heavy Oil Processing Institute of New Energy China University of Petroleum (East China) Qingdao 266580 China Shandong Key Laboratory of Biochemical Analysis College of Chemistry and Molecular Engineering Qingdao University of Science and Technology Qingdao 266042 China 

基　　金：supported by the Natural Science Foundation of Shandong Province(ZR2017MB059) the Major Program of Shandong Province Natural Science Foundation(ZR2018ZC0639) the National Natural Science Foundation of China(21776314) the Fundamental Research Funds for the Central Universities(18CX05016A) the Postgraduate Innovation Project of China University of Petroleum(YCX2018074) 

出 版 物：《Science China Materials》 (中国科学（材料科学（英文版）)

年 卷 期：2019年第62卷第9期

页      码：1285-1296页

摘      要：本文以三元金属钴-镍-铁普鲁士蓝结构纳米立方体(Co0.9-Ni0.9Fe1.2NCs)为前驱体,通过简单气相磷化处理,得到优化比例的P-Co0.9Ni0.9Fe1.2纳米立方体磷化物,其具有高本征活性、导电性和高缺陷密度的特点. SEM和TEM结果表明,碳掺杂型P-Co0.9Ni0.9-Fe1.2保持了纳米立方体的结构,其粗糙的表面结构意味着丰富的缺陷位,暴露更多真实活性位.三元金属普鲁士蓝前驱体的磷化处理不仅提供了碳掺杂,而且原位构筑了立方体表面缺陷位.碳掺杂降低了电荷传输的阻抗,优化了电子传输速率.三元金属离子之间的协同作用以及丰富的缺陷活性位有效提高了电催化的性能.P-Co0.9Ni0.9Fe1.2拥有极其高的HER和OER催化活性,仅需要-200.7 mV(HER)和273.1 mV(OER)过电位就可以达到10 mA cm-2的电流密度.其全水分解仅需1.52 V就可以达到10 mA cm-2的电流密度.此外,本文还对催化剂的稳定性进行了测试.本工作为设计高效过渡金属基双功能电解水催化剂提供了一种简便方法.

主 题 词：表面缺陷 立方体 碳掺杂 水分解 磷化物 掺杂型 纳米 三元 