Ti-Zr-Cu-Ni-Fe-Co-Mo钎料合金钎焊γ-TiAl/GH536接头的显微组织与剪切强度

作     者：李力 赵巍 冯志雪 孙佳 李小强 Li LI;Wei ZHAO;Zhi-xue FENG;Jia SUN;Xiao-qiang LI

作者机构：华东交通大学材料科学与工程学院南昌330013 华南理工大学国家金属材料近净成形工程技术研究中心广州510640 中车南京浦镇车辆有限公司转向架设计部南京210031 

基　　金：Project(51865012)supported by the National Natural Science Foundation of China Project(20202BABL204040)supported by the Natural Science Foundation of Jiangxi Province,China Project(2016005)supported by the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,China Project(GJJ170372)supported by the Science Foundation of Educational Department of Jiangxi Province,China Project(JCKY2016603C003)supported by the GF Basic Research Project,China Project(JPPT125GH038)supported by the Research Project of Special Furnishment and Part,China 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2020年第30卷第8期

页      码：2143-2155页

摘      要：采用Ti-Zr-Cu-Ni-Fe-Co-Mo作为钎料,在钎焊温度1090~1170℃、钎焊时间0~20 min的工艺参数下,实现γ-TiAl和GH536合金的钎焊连接,利用SEM、EDS、XRD和万能试验机研究钎焊温度和钎焊时间对钎焊接头显微组织和剪切强度的影响。结果表明:不同工艺参数下获得的γ-TiAl/GH536钎焊接头均包括4个界面反应层。随着钎焊温度的升高和钎焊时间的延长,钎缝宽度和钎焊接头的平均抗剪强度均是先增大后减小。钎焊温度1150℃、钎焊时间10 min时获得的钎焊接头的剪切强度最大,达262 MPa。Al3NiTi2和TiNi3脆性金属间化合物是产生裂纹和降低接头强度的主控因素,Al3NiTi2脆性金属间化合物几乎占据整个呈典型解理断裂特征的剪切断口表面。

主 题 词：γ-TiAl合金 镍基高温合金 真空钎焊 非晶钎料 显微组织 剪切强度 