摘要：In order to evaluate interstitial strengthening effect on the properties of high entropy alloy(HEA),a nitrogen-doped Cr Mn Fe VTi6 HEA was fabricated by mechanical alloying(MA)and spark plasma sintering(SPS).XRD,SEM,TEM and FIB were used to characterize the phase composition and microstructure of this *** sintered bulk HEA exhibits a microstructure comprising TiNx,BCC,Laves and B2 *** HEA exhibits high yield strength(>2729 MPa)and hardness in lower temperature range of<380℃.Quantitative calculations of the contributions from each strengthening mechanism in the BCC phase indicate that the interstitial strengthening by nitrogen is the dominant *** additions in the BCC phase can produce a yield strength increase of-634 MPa/at.%,which is much higher than the strengthening effects of carbon or boron additions in other *** demonstrates that adding nitrogen is a viable approach for enhancing the strength of HEAs.

摘要：本文针对垂直起降的可重复使用运载器(RLV)返回着陆段面临多类型复合风场干扰影响导致的姿态跟踪控制收敛时间上界与初始状态强耦合及跟踪性能严重下降等问题,提出一种基于双幂次固定时间稳定理论的快速高精度控制方法。首先,对可重复使用运载器返回着陆段所受的自然风场进行分类建模,并分析风场对着陆段姿态控制的影响;其次,基于反步法框架,设计高低幂次加权多项式形式的趋近律,以保证系统状态误差在固定时间内收敛,且收敛时间和上界与初始状态无关;同时,为降低风场扰动对着陆段控制系统性能的影响,保证着陆段控制性能的稳定性及着陆安全性,引入固定时间扩张状态观测器对风场扰动进行估计和补偿;最后基于Lyapunov理论,证明了所设计的控制律可使RLV返回着陆段姿态控制误差在固定时间内收敛;多组数值仿真验证了所提方法的有效性。

摘要：对镍基高温合金GH536进行了室温拉伸试验(加载速率分别为0.06mm/min,0.6mm/min,3.6 mm/min和36mm/min),研究其在室温拉伸变形过程中的锯齿流变行为.结果表明:合金在低于3.6 mm/min的加载速率下,由于合金中原始退火孪晶界对位错滑移的阻碍作用,在其应力-应变曲线上出现了以B型锯齿为主的A型、B型两种锯齿,且在拉伸变形后合金内原始退火孪晶界出现了不同程度的变形;当加载速率为36mm/min时,由于位错滑移速度加快,孪晶界与快速移动的位错相遇后发生分解,孪晶界几乎消失,锯齿效应变得不明显;此外,在不同加载速率和应变下,合金应力-应变曲线上锯齿的振幅大小不同,这主要与移动和固定位错的密度相关.

摘要：以耐高温酚醛树脂为基体,石英纤维为增强体,热膨胀型微胶囊及空心玻璃微珠为填料,通过模压法和热膨胀法相结合制备了新型石英纤维增强酚醛多孔复合材料。采用扫描电镜、热重分析及力学性能测试,研究了不同热膨胀型微胶囊含量对复合材料微观组织及性能的影响,并通过断口形貌分析,揭示了该多孔材料的结构失效模式。结果表明:采用热膨胀法制备的隔热材料泡孔结构完整,闭孔率高,材料的隔热性能优异。当热膨胀型微胶囊含量为20wt%时,材料的综合性能最好,进一步提高微胶囊含量会导致开孔空隙率升高,材料的隔热性能降低。材料的断口形貌分析表明,复合材料中石英纤维与基体结合良好,界面强度适中,材料在拉伸和压缩应力下表现出非脆性断裂特征。