摘要：提出了ZnSe/ZnS多量子阱光开关的综合优化设计方案。根据Kronig-Penney模型对多量子阱结构进行优化,根据实验结果对多量子阱构成的非线性F-P进行了优化设计。

摘要：设计了(CdZnTe,ZnSeTe)/ZnTe复合量子阱结构,并用吸收光谱、室温光致发光谱和飞秒脉冲抽运-探测方法研究了该复合结构中的激子隧穿过程.分别测量了该结构中CdZnTe/ZnTe量子阱层和ZnSeTe/ZnTe量子阱层中激子衰减时间.观察到从CdZnTe/ZnTe量子阱层向ZnSeTe/ZnTe量子阱层的快速激子隧穿,隧穿时间为5.5 ps.

摘要：通过介电泳方法定向排列了ZnO纳米线,制作了自组装有序的纳米线紫外探测器。为了适合在金叉指电极上排列,用水热方法设计生长了超长的ZnO纳米线,并通过700℃的热退火处理,使得可利用的表面缺陷增多。通过研究器件的光致发光光谱和光响应,发现光、暗电流比和响应恢复时间有显著提高,并分析了其中可能的机理。

摘要：设计并制备了一种新型的（ＣｄＺｎＴｅ，ＺｎＳ）／ＺｎＴｅ复合量子阱结构。使ＣｄＺｎＴｅ 量子阱中的激子有可能在短时间内隧穿到ＺｎＳ 阱层，从而达到提高光双稳器件“关”速度的目的。并通过对发光特性的研究证实在我们设计的结构中横向激子隧穿的存在，从而为进一步研究超高速光开关提供了实验依据。

摘要：对不同加速电压电子束泵浦下的ZnO/Zn0.85Mg0.15O量子阱的荧光光谱进行了研究。样品利用分子束外延技术在蓝宝石衬底上生长。激子隧穿使非对称双量子阱的激发效率相对于对称阱有了明显提高。非对称阱的结构设计使最佳激发电压从对称阱的7 kV降低到了更适合器件小型化的5 kV。

摘要：Nanocarbon as an eco-friendly and abundant material has strong multi-color fluorescence, which makes it a promising candidate for healthy lighting and display. However, the low fluorescence efficiency and poor stability of multi-color carbon nanoparticle（CNP） phosphors are main hurdles that hinder their applications. This work demonstrated efficient and stable multi-color CNP phosphors through synergy between inner polar groups and outer silica matrix. The polar groups in polyethylene glycol（PEG） 6,000 are favor of high fluorescence of the CNP phosphors, and the low melting point（64℃） of PEG 6,000 helps to improve the thermal stability of the phosphors, while the silica matrix provides protection to the phosphors. Based on this design,blue, green, yellow and red CNP phosphors with photoluminescence quantum yield of 53.1%, 47.4%, 43.8% and 42.3% have been achieved, all of which are the best values in ever reported multi-color CNP phosphors. Furthermore, the fluorescence of the CNP phosphors keeps almost unchanged at 100℃ and degrades little in one month, indicating their good thermal tolerance and temporal stability. In addition, multicolor devices including white light-emitting devices（LEDs）have been realized by coating the CNP phosphors onto UV chips. The luminous efficiency, correlated color temperature,Commission Internationale de L＇Eclairage and color rendering index of the white LED can reach 12 lm W^-1, 6,107 K,（0.32, 0.33） and 89, respectively, indicating the potential applications of the CNP phosphors in lighting and display.

摘要：提出结合Ｃｄ（ＯＨ）２ 选择性包覆与光分解腐蚀法缩小ＣｄＳ纳米微粒的尺寸分布， 并通过对ＣｄＳ纳米微粒发射光谱的研究证实了这一设计思想． 以多聚磷酸钠（ＨＭＰ）为稳定剂合成ＣｄＳ纳米微粒， 再通过Ｃｄ２＋ 与ＯＨ－ 的选择性包覆在大粒径的ＣｄＳ纳米微粒表面形成一层Ｃｄ（ＯＨ）２， 然后溶液置于日光下辐照处理， 数天后， 未经包覆的小粒径ＣｄＳ纳米微粒被日光腐蚀分解， 溶液中只剩下被Ｃｄ（ＯＨ）２ 包覆的大粒径ＣｄＳ纳米微粒， 这样即可达到缩小ＣｄＳ纳米微粒尺寸分布的目的．

摘要：设计制作了一种Au/ZnO/Al结构的紫外探测器,光的入射方式采用背入射式。ZnO薄膜是用磁控溅射在蓝宝石衬底上制备的。I-V测试表明：Au与ZnO形成了肖特基接触。得到探测器的光响应峰值在352nm,截止边为382nm,可见抑制比达一个量级。由于该探测器是一种垂直结构器件,对于进一步实现ZnO紫外探测器阵列及单光子探测有很好的研究价值。