摘要：A novel Cu?6.5Ni?1Al?1Si?0.15Mg?0.15Ce alloy with super-high strength was designed and its corrosion behavior in3.5%NaCl solution at25°C was investigated by the means of SEM observation,TEM observation and XPS *** alloy after solution treatment,80%cold rolling and aging at450°C for1h had the best comprehensive properties with hardness of HV314,electrical conductivity of19.4%IACS,tensile strength of1017MPa,and average annual corrosion rate of0.028mm/*** oxides and chloride products formed at first,followed by the formation of dyroxides *** alloy showed super-high strength,good electrical conductivity and corrosion resistant because Ni2Si hindered the precipitation of large NiAl at the grain boundary and the denickelefication of the alloy.

摘要：超高强弹性铜合金是导电弹性元器件的关键材料之一,它广泛应用在电子电工、通信导航、汽车工业和海洋工程等领域。综述了超高强铜合金材料的研究开发现状,以强度超过1000 MPa的Cu-Be、Cu-Ti、Cu-Ni-Sn、CuNi-Mn、Cu-Ni-Si和Cu-Ni-Al合金为例,概述了它们的合金化设计原则,时效过程中的相变机理,包括相变贯序、析出相的分布、取向关系等,同时对它们的制备特点、主要应用领域、强化机制和相关物理性能进行了阐述,在此基础上对它们开发应用中所存在的问题、前景和市场需求进行了分析和展望。

摘要：综述了Cu-Ni-Si系合金开发原理、成分设计及制备工艺,归纳总结了该合金性能与Ni、Si元素的质量比值、添加合金元素的种类和数量以及制备技术之间的关系,并介绍了不同工艺路线下Cu-5.2Ni-1.2Si合金时效后硬度和导电率的变化规律。

摘要：综合学生所做的几个电学实验,以"用示波器观察二极管伏安特性曲线"设计性实验为例,探讨如何提高学生综合运用所学知识和解决实际问题的能力.

摘要：设计并制备Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce(wt.%)合金。采用光学显微镜(OM)、扫描电镜(SEM)、能谱分析和透射电镜(TEM)等测试手段研究合金形变热处理过程中微观组织及性能的变化。合金铸态组织为典型的枝晶组织,铸锭经过920℃热轧后,枝晶组织显著消除。合金的适宜固溶处理制度为960℃/4 h。该合金固溶处理后的冷变形对合金最终性能有很大影响。冷变形程度越大,合金达到硬度峰值的时间越短,硬度峰值和电导率越高。时效温度越高,时效析出过程越快。960℃固溶4 h后冷轧50%,450℃时效2 h硬度峰值可达300.8 HV,电导率20.6%IACS,抗拉强度963.9 MPa,屈服强度950.1 MPa。合金在时效过程中析出纳米级粒子为δ-Ni2Si,其与基体的位相关系为:Cuδ[001][001],Cuδ(110)(010),Cuδ(1 10)(100)。

摘要：测量杨氏弹性模量是大学物理实验的一个重要实验,也是材料力学中衡量固体材料抗形变能力的重要物理量,还是选定机械构件材料的依据之一和工程技术中常用的参数.杨氏弹性模量通常用镜尺法进行测量,此方法的系统误差较大,根据近千份实验报告统计,其相对误差达5%。本文介绍一种新的杨氏弹性模量测量方法。该方法利用激光束照射光杠杆镜面,用高灵敏度的线型固态CCD图像传感器自动接受激光光束偏转方位来取代传统的依靠人眼从望远镜读数中获取数据的方法,实现了过程自动化,从而消除了测量过程中所产生的人为因素的影响。该方法实验测量杨氏弹性模量的相对误差为0.88%,大大提高了测量精度。这一技术可直接运用于有关材料的杨氏模量测量,并将传统的物理实验改进成了一个有意义的集设计、研究、综合于一体的实验。