摘要：The multi-component composition characteristics of high-temperature near-α Ti alloys were investigated in the present work by means of a cluster formula approach. The uniform cluster formula [CN12 cluster](glue atom)3 for the hexagonal close-packed α solid solution was first obtained based on the Friedel oscillation theory, with a total atom number in the formula of Z = 16. Then it was analyzed that the Z values in the cluster composition formulas of typical near-α Ti alloys are within the range of Z = 16.0016.30, being perfectly consistent with the ideal Z = 16. Based on it, a series of new alloys with Z = 16 and with Nb/Ta substitution for Mo in Ti1100 alloy were designed, suction-cast into φ 6 mm rods, and then heat-treated with solid solution and aging. It was found that the alloy with co-addition of Mo, Ta and Nb has a high strength and good ductility at both room and high temperatures. More importantly, the additions of Nb and Ta can contribute to the formation of continuous and compact Al2O3 scales, resulting in an obvious improvement of oxidation resistances at both 923 K and 1073 K. The effects of Mo, Ta and Nb on the oxidation behaviors of the designed alloys at 1073 K were further discussed.

摘要：用团簇加连接原子模型设计了系列用于制作引线框架的Cu-Ni-Si合金。在Cu含量小于95%的浓溶质区,采用单团簇模型[(Ni2/3Si1/3)-Cu12]Cu1~6设计合金成分;在Cu含量大于或等于95%的稀溶质区,采用双团簇模型{[(Ni2/3Si1/3)-Cu12]Cu3}A+{[Cu-Cu12]Cu3}B设计合金成分。利用XRD、OM、TEM、Vickers硬度计、电导率测量仪等实验获得Cu-Ni-Si合金的成分规律。结果表明,在Cu-Ni-Si合金的成分范围内存在Cu含量为95.0%~95.8%的成分敏感区,此区间内合金同时存在时效析出强化和调幅分解强化,致使Vickers硬度突然增加,导电率降低,两者变化趋势相反,且与成分之间无规律性依赖关系。成分敏感区前后的浓溶质区和稀溶质区的合金中,不存在调幅分解强化,Vickers硬度(H)随Cu含量(CCu)增加而减少,分别满足H=-12.6CCu+1362.7和H=-26.2CCu+2777.3的线性关系;相应的导电率(σ)随CCu的线性增加关系分别为σ=0.2CCu+28.6和σ=5.2CCu-466。

摘要：用团簇成分式方法对Fe-Cr-Al-Mo-Nb合金进行成分解析,并在此基础上确定了Fe-Cr-Al三元基础成分式Fe_(75)Al_(9.375)Cr_(15.625)(at.%),进而添加Mo、Nb、Ta和Zr元素替代部分Cr元素。采用真空电弧熔炼制备设计的母合金锭,然后进行1200℃/2 h固溶处理,进而在800℃进行多道次热轧成板,再进行800℃/24 h时效处理,最后在不同温度进行高温固溶处理,研究了微量元素添加对合金高温组织稳定性的影响。结果表明,对于800℃/24 h时效的Mo/Nb/Ta/Zr合金化样品,第二相(Laves相)粒子均弥散分布于铁素体基体中。1000℃/1 h再固溶处理,使系列合金中的第二相粒子发生回溶,至1200℃/1 h固溶后只含有Mo/Nb的合金中的第二相粒子已全部溶入到基体中,而在Ta和Zr微合金化的样品中仍有第二相粒子存在于基体的晶界处,有效抑制了基体晶粒在高温下异常长大,从而提高基体的组织稳定性和合金在高温下的力学性能。

摘要：一、虚拟博物馆的定义和发展对于虚拟博物馆,维基百科中这样解释:'虚拟博物馆(或称数字博物馆),是以博物馆为主题,结合多媒体技术应用的展示平台。虚拟博物馆浏览自由,交互简易,可收藏任何被数字化的事物,信息可以在网络平台上不断被更新与提供服务,通过信息技术设计出类似于传统博物馆的形态,并向受众提供一种全新的展示方式与参观体验。

摘要：利用固溶体合金中的"团簇加连接原子"模型解析了典型高温近α-Ti合金Ti1100的成分,其团簇成分式为[Al-(Ti_(13.7)Zr_(0.3)](Al_(0.69)Sn_(0.18)Mo_(0.03)Si_(0.12)。在此基础上,采用相似元素替代原则设计了微量元素Hf、Ta和Nb添加的系列合金成分,即[Al-(Ti_(13.7)Zr_(0.15)Hf_(0.15))](Al_(0.69)Sn_(0.18)Si_(0.1)(Mo/Ta/Nb)_(0.03))。对该系列合金进行950℃,1h固溶+560℃,6h时效处理,然后进行组织结构、硬度、抗高温氧化及电化学腐蚀性能测试。结果表明Zr_(0.15)Hf_(0.15),合金与参比合金具有相同片层β转变组织,而在此基础上Ta和Nb的添加会使合金中产生大量等轴α组织;但组织的改变对系列合金的显微硬度影响不大,介于3300~3700MPa。650℃氧化100 h后系列合金均具有较强的抗氧化能力,氧化增重小于1.0mg/cm^2,而在800℃氧化100h后,添加Hf、Ta、Nb元素的合金氧化增重明显低于Ti1100合金,氧化层厚度为23~27μm,且氧化层致密,其中[Al-(Ti_(13.7)Zr_(0.15)Hf_(0.15))](Al_(0.69)Sn_(0.18)Si_(0.1)Ta_(0.015)Nb_(0.015))合金具有最优的抗高温氧化性能,800℃,100h后的氧化增重仅为2.6mg/cm^2。此外,该系列合金在在3.5%NaCl溶液中也具有较好的耐蚀性。

摘要：在"绿色经济、低碳经济"大背景下,国网公司提出"两型一化"电力设备的建设要求,即环境友好型、资源节约型、工业化要求,智能化预装式变电站在配电网中则是发电机组接入电网的关键组成部分。基于物联网技术设计了预装式变电站主电量数据硬件监测系统,实现对预装式变电站主电量数据实时监测、无线传输和数据处理。分析预装式变电站主设备健康评估技术需求,引入模糊综合评判法、神经网络算法、灰色关联理论和DS信息融合技术,提出基于预装式变电站主设备的健康评估模型,实现对机组运行的健康评估,为智能化预装式变电站安全鉴定提供参考依据。仿真结果表明,该方法是切实可行的。

摘要：以单羟基氟碳链一元醇为有机氟改性剂,将含氟基团引入聚氨酯主链中,通过分子设计的方法制备出软段含有离子基团的有机氟阴离子型水性聚氨酯。比较了传统水性聚氨酯、硬段含氟的水性聚氨酯和软段含氟的水性聚氨酯在合成方法、耐水性、热稳定性以及结晶性方面的差异;实验证明了软段含氟聚氨酯的水性聚氨酯的性能最为优良。通过红外光谱的表征确定了氟化聚氨酯的结构,并证明了含氟基团的引入对聚氨酯软硬段间氢键作用的影响;水接触角由73°增加至107°,吸水溶胀率降低了66%,胶膜耐水性提高;热重分析结果表明,含氟聚氨酯的最大热失重温度提高了30℃,热稳定性增加;广角X射线衍射结果表明,胶膜的结晶度增加,结晶形式发生了微小程度的转变;扫描电子显微镜结果证明存在不均匀的多相结构。

摘要：目的·探讨使用超低剂量CT (ultra-low-dose CT, ULDCT)平扫评价基于实体瘤疗效评价标准(response evaluation criteria in solid tumors,RECIST)定义的肺部靶病灶和磨玻璃结节的可行性。方法·2020年4月-6月纳入接受了胸部ULDCT平扫(0.07~0.14 mSv)和低剂量增强CT检查(2.38 mSv),而且有RECIST标准定义的可测量肺部靶病灶或直径≤1 cm磨玻璃结节的患者。每例患者均重建了4组图像,包括3组ULDCT图像,分别为80%强度的多模型自适应统计迭代重建(adaptive statistical iterative reconstruction-V with an 80%strength level,ASIR-V-80%)图像、中等强度的深度学习重建(deep learning image reconstruction of moderate strength,DLIR-M)图像和高强度的深度学习重建(deep learning image reconstruction of high strength,DLIR-H)图像,以及1组作为参考标准的增强CT图像。结果·80例患者符合入组标准,平均年龄(62±11)岁,共80个靶病灶和27个磨玻璃结节。3组ULDCT图像的肺部靶病灶测量值(r分别为0.988、0.987和0.990)、≤1 cm磨玻璃结节的直径测量值(r分别为0.905、0.906和0.969)、非肺门淋巴结靶病灶测量值(r分别为0.969、0.957和0.977)、肺门淋巴结靶病灶测量值(r分别为0.972、0.994和0.994)与增强CT有很高的相关性。Bland-Altman分析显示,DLIR-H重建图像中肺部靶病灶测量值的大小与参考值的差异为4.3%(95%一致性界限:-5.7%~14.3%),非肺门淋巴结靶病灶测量值的大小与参考值的差异为5.1%(-9.1%~19.3%),优于ASIR-V-80%[8.5%(-3.3%~20.3%),9.7%(-6.0%~25.3%)]和DLIR-M [8.5%(-4.2%~21.3%,8.8%(-9.9%~27.5%)]。DLIR-H重建图像中的肺门淋巴结病灶测量值大小与参考值的差异为18.3%(8.8%~27.9%),优于ASIR-V-80%[20.2%(-1.2%~41.5%)]和DLIR-M [23.4%(13.5%~33.2%)]。DLIR-H重建图像中磨玻璃结节测量值与参考值的差异为7.0%(-5.7%~19.7%),优于ASIR-V-80%[14.4%(-4.4%~33.2%)]和DLIR-M [16.3%(-4.1%~36.7%)]。结论·基于DLIR-H重建的ULDCT平扫图像中的肺部靶病灶和直径≤1 cm磨玻璃结节的测量值与增强CT图像有很高的相关性和较低的差异性,有利于在大幅度降低辐射剂量下对肿瘤和磨玻璃结节进行重复扫描。

摘要：创新人才自主培养是提高国家人才竞争力和科技创新能力的重要途径。从人才自主培养的核心要素、关键环节和动力来源方面,提出创新人才自主培养的理论逻辑。以霍恩海姆大学为研究对象,剖析其创新人才自主培养方面的实践逻辑,包括依据国家战略和社会需求发展新专业;遵循人才知识结构和能力要求提供模块化课程及咨询服务;依托全球合作网络提升学校国际化水平等。霍恩海姆大学的创新人才自主培养有其独特性,呈现出专业建设顺势而动、课程设计灵活配置、产学研深度融合、聚焦实践平台和资源整合、依托合作网络加强横向融通等新特征。

摘要：近年来,中、美、加、日等国进行了多海域、多频次、多类型天然气水合物藏的防砂完井实践与探索,结果表明,砂堵问题仍是制约其长效开采的关键因素。文章基于神狐海域水合物藏储层特征、出砂机理分析、疏松砂岩防砂实践以及神狐海域防砂探索(2017和2020年)经验,研究并剖析了现有筛管完井技术在泥质粉砂岩水合物藏储层中的应用局限性,首次提出了基于井口打压井下周期解堵的“自清洁”精密复合防砂筛管设计构思,并就其自清洁原理、应用前景进行了分析说明,优化设计了筛网尺寸及挡砂精度;此外,文章还对该筛管核心部件“冲砂管”的结构、材质、开孔方式以及冲砂周期进行了优化研究。文章中的“自清洁”防砂筛管研究是长效防砂完井的一次创新探索,旨在推动水合物藏开发进程。