摘要：The rational design and construction of inexpensive and highly active electrocatalysts for hydrogen evolution reaction(HER)is of great importance for water ***,we develop a facile approach for preparation of porous carbon-confined Ru-doped Cu nanoparticles(denoted as Ru-Cu@C)by direct pyrolysis of the Ru-exchanged Cu-BTC metal–organic *** served as the electrocatalyst for HER,strikingly,the obtained Ru-Cu@C catalyst exhibits an ultralow overpotential(only 20 mV at 10 mA cm^(-2))with a small Tafel slope of 37 m V dec^(-1)in alkaline *** excellent performance is comparable or even superior to that of commercial Pt/C *** functional theory(DFT)calculations confirm that introducing Ru atoms into Cu nanocrystals can significantly alter the desorption of H_(2) to achieve a close-to-zero hydrogen adsorption energy and thereby boost the HER *** strategy gives a fresh impetus to explore low-cost and high-performance catalysts for HER in alkaline media.

摘要：目前,核用低中子截面型高熵合金还存在绝对强度不足的瓶颈难题。为实现核用低中子截面型高熵合金力学性能的大幅提升,本研究通过电弧熔炼制备了AlZrNbMo系BCC结构高熵合金,压缩力学性能测试发现高温固溶处理后AlZrNbMo高熵合金的强度同铸态相比提升了31%,达到了约2210 MPa。通过对比分析铸态及1200℃高温固溶后AlZrNbMo高熵合金的相组成、元素分布等微观组织,发现1200℃高温热处理后,AlZrNbMo高熵合金的晶内相区域Nb、Mo含量大幅度提升,导致基体相的晶格畸变增大,利于强度的显著升高;同时,原始铸态组织中的晶间黑色区域为富Zr单质颗粒,强度相对较低;随着高温热处理后的迅速淬火,由于元素的迁移扩散导致高硬度AlZr金属间化合物相的生成,同样利于合金强度的大幅度提升。相关结果将为新型超高强度核用高熵合金的设计提供理论参考和设计依据。

摘要：基于电弧熔炼法将可燃毒物硼(B)元素添加到AlNbMoZr基难熔高熵合金(RHEA)中,制备出一种具有中子毒物特性的高强度新型核用RHEA材料。对其进行强度为4 MeV的Kr离子辐照实验,研究了这种材料的Kr离子辐照损伤行为。室温压缩结果表明,AlNbMoZrB合金具有优异的力学性能,其压缩屈服强度可达1180 MPa,压缩强度约为1274 MPa,塑性约为4.8%。对辐照前后这种合金的相结构和显微组织演化的分析结果表明,AlNbMoZrB合金具有典型的枝晶组织,其中枝晶区为无序BCC结构基体相,枝晶间区由FCC结构的Al-Zr相及α-Zr相组成,经Kr离子辐照后α-Zr相发生非晶化转变,还产生了高密度和1/2型位错环。在室温辐照条件下位错环的体积密度约为4.11×10^(22)m^(-3),尺寸为12~16 nm;在300℃辐照条件下位错环的体积密度降低到约1.63×10^(22)m^(-3),尺寸增大到23~27 nm。

摘要：对磁控溅射法制备的AlNbTiZr中熵合金涂层在500℃下进行了不同时间(0~150 h)的真空等温退火。采用XRD、SEM及纳米压痕和纳米划痕的分析手段研究了等温退火对涂层显微组织演变和力学性能的影响。结果表明:经500℃/150 h退火后涂层相结构出现了结晶现象。涂层经60 h等温退火后其硬度和弹性模量均达到最大值为10.7 GPa和152.7 GPa,而90 h和150 h热处理后硬度和弹性模量均有所下降。随着等温退火时间的延长,塑性变形能力和断裂韧性有所提高。Al、Nb和Ti元素在界面处的相互扩散加剧,界面结合强度有较大提升。这均有利于涂层适应压水堆苛刻的工作条件。

摘要：利用能量为6 MeV、注量为2.3×10^(15)Au/cm^(2)的Au离子对磁控溅射法制备的Cr和CrNb涂层进行离子辐照。采用XRD、SEM及TEM等分析技术研究辐照对4种不同Nb含量的涂层微观结构和力学性能的影响。结果表明:随着Nb含量增加,晶格畸变导致衍射峰偏移,晶体转变为非晶,经离子辐照后涂层相结构出现了结晶现象。辐照令4种涂层表面形貌更光滑,同时TEM分析发现辐照区域微观组织结构变化不明显,表现出良好的抗辐照性能。Nb元素加入到Cr基涂层中,能提高涂层硬度模量和塑性变形能力,其中Cr_(0.92)Nb_(0.08)涂层具有最大值(硬度13.7 GPa、弹性模量204.2 GPa),经过离子辐照后的涂层均表现出较沉积态更高的硬度模量,这是辐照硬化导致。Cr基涂层中加入Nb元素能增加涂层力学性能,并未降低涂层的抗辐照性能,同时Cr_(0.82)Nb_(0.18)涂层在4种涂层中的抗辐照性能较好。

摘要：采用等离子熔覆技术在45号钢基体表面制备FeCoCrNiAl高熵合金涂层,研究熔覆电流和离子气流量对涂层表面形貌及孔隙率的影响。结果表明,当熔覆电流为180 A、离子气流量为2.5 L/min、熔覆速度为100 cm/min时,制备出的FeCoCrNiAl合金涂层与基体结合良好、无裂纹,孔隙率达到最低值0.0276%。该工艺制备的FeCoCrNiAl合金涂层高熵效应显著,但组织中除了具有BCC结构相以外,还存在具有FCC结构的Fe-Cr相、Ni-Co相、富Ni相、富Al相等成分。FeCoCrNiAl高熵合金涂层的显微硬度为500 HV,达到45钢基体的2倍以上。

摘要：采用电弧熔炼法成功制备了Nb_(50)Mo_(30)Zr_(20)及(Nb_(50)Mo_(30)Zr_(20))_(100-x)Cr_(x)(x=5、10、15,对应Cr5、Cr10及Cr15)合金,并系统研究了Cr含量对相结构、微观组织与力学性能的影响规律。研究结果表明,Cr元素的添加使NbMoZr合金由单一BCC结构相组织转变为富Mo、Nb的BCC基体相与富Zr、Cr、Nb的Laves相组成的双相组织,同时二次枝晶壁间距也逐渐减小。X射线衍射(XRD)和透射电子显微镜(TEM)分析表明,Laves相对应于FCC结构的Cr_2(Nb,Zr)相。因此,随着Cr含量的增加,压缩屈服强度逐渐从NbMoZr合金的1288 MPa提升至Cr15合金的1924 MPa,Laves相诱导的第二相强化以及枝晶细化导致的细晶强化是强度提升的主要机制。对比三种含Cr合金,发现Cr10合金表现出最优的强塑性匹配,屈服强度1690MPa,塑性应变9.0%,有望成为弥散性核燃料金属基体的有利候选材料之一。

摘要：锆合金中的第二相是影响其力学性能和耐腐蚀性能的主要因素,开展国产新锆合金不同温度环境中的第二相研究对事故等特殊工况下的服役性能预测具有非常重要的意义。通过加热锆合金样品至500,700,900℃,并保温1 h,随后采用不同冷却速率进行降温,并用TEM对第二相结构及元素组成进行分析,结果表明:900℃时,样品中第二相结构均为体心正方结构Zr2Fe;500℃和700℃时,样品第二相为密堆六方结构Zr(FeCrNb)2和面心立方结构Zr3Fe。Zr-Nb-Fe-Cr第二相在不同温度析出都是以密堆六方结构的ZrCr2为基本骨架,由Nb,Fe替换Cr得到。第二相中Fe和Cr的原子个数比随着温度的升高而不断增加。冷却速率越快时,Fe来不及充分扩散,将形成少部分面心立方结构Zr3Fe。

摘要：通过对比试验验证甘蔗电动割刀作业效果,推动解决我国甘蔗收获机械化率长期低位问题。2024年12月,农业农村部农业机械化总站与广西壮族自治区农业机械化服务中心在广西柳州,对甘蔗电动割刀与人工“一刀砍”进行了作业性能与经济性能的全面测定。结果显示,甘蔗电动割刀适用于丘陵陡坡地等小地块,能显著降低宿根破头率,但对割茬损失率改善不明显,且作业效率和总作业成本相较人工存在劣势。因此,甘蔗电动割刀可作为甘蔗机收辅助工具,在特定地块条件下发挥作用,但需进一步优化设计以提高其效率和经济性,满足甘蔗机械化收获需求。

摘要：对鬼像的基本概念和形成原因进行了介绍与分析,提出了利用光学设计软件CODE V定性分析与光机适配性软件LightTools定量分析相结合的鬼像仿真分析方法。使用lightTools软件仿真与系统探测器归一化真实响应照度值相比较找出鬼像路径,给出改进措施。对验证实验中给定的电视成像光学镜头的鬼像路径进行计算和仿真,计算结果表明,镜头轴上鬼像路径的归一化响应照度为3.5×10^(-5),小于探测器的归一化响应范围9.85×10^(-5)~1,探测器无响应,即不产生鬼像,证明该仿真分析方法正确可行。