摘要：The development of an efficient artificial H_(2)O_(2)photosynthesis system is a challenging work using H_(2)O and O_(2)as starting ***,3D In2.77S_(4)nanoflower precursor was in-situ deposited on K^(+)-doped g-C_(3)N_(4)(KCN)nanosheets using a solvothermal method,then In2.77S_(4)/KCN(IS/KCN)het-erojunction with an intimate interface was obtained after a calcination *** investigation shows that the photocatalytic H_(2)O_(2)production rate of 50IS/KCN can reach up to 1.36 mmol g^(-1)h^(-1)without any sacrificial reagents under visible light irradiation,which is 9.2 times and 4.1 times higher than that of KCN and In2.77S_(4),*** enhanced activity of the above composite can be mainly attributed to the S-scheme charge transfer route between KCN and In2.77S_(4)according to density functional theory calculations,electron paramagnetic resonance and free radical capture tests,leading to an expanded light response range and rapid charge separation at their interface,as well as preserving the active electrons and holes for H_(2)O_(2)***,the unique 3D nanostructure and surface hydrophobicity of IS/KCN facilitate the diffusion and transportation of O_(2)around the active centers,the energy barriers of O_(2)protonation and H_(2)O_(2)desorption steps are ef-fectively reduced over the *** addition,this system also exhibits excellent light harvesting ability and *** work provides a potential strategy to explore a sustainable H_(2)O_(2)photo-synthesis pathway through the design of heterojunctions with intimate interfaces and desired reac-tion thermodynamics and kinetics.

摘要：Ag nanoparticles (NPs) were deposited on the surface of g-C3N4 (CN) by an in situ calcination method. NiS was successfully loaded onto the composites by a hydrothermal method. The results showed that the 10 wt%-NiS/1.0 wt%-Ag/CN composite exhibits excellent photocatalytic H2 generation performance under solar-light irradiation. An H2 production rate of 9.728 mmol·g^-1·h^-1 was achieved, which is 10.82-, 3.45-, and 2.77-times higher than those of pure g-C3N4, 10 wt%-NiS/CN, and 1.0 wt%-Ag/CN composites, respectively. This enhanced photocatalytic H2 generation can be ascribed to the co-decoration of Ag and NiS on the surface of g-C3N4, which efficiently improves light harvesting capacity, photogenerated charge carrier separation, and photocatalytic H2 production kinetics. Thus, this study demonstrates an effective strategy for constructing excellent g-C3N4-related composite photocatalysts for H2 production by using different co-catalysts.

摘要：硒化锑(Sb_(2)Se_(3))属于窄带隙半导体材料,具有良好的光吸收特性,已逐渐应用于光电催化领域.独特的一维(Sb_(4)Se_(6))_(n)带状结构单元连接方式,使其载流子传输具有高度各向异性.本文通过气相输运沉积法和原位水热法成功构建了还原氧化石墨烯(rGO)修饰的准一维Sb_(2)Se_(3)@In_(2)S_(3)光陷阱异质结.研究结果表明,在rGO空间限域效应下,原位生长的非层状In_(2)S_(3)纳米片厚度从30 nm减小到10 nm,显著增加了光电极的电化学活性比表面积,进一步增强了光陷阱纳米结构对光的捕获能力.rGO和超薄In_(2)S_(3)纳米片共同修饰的准一维毛刷状Sb_(2)Se_(3)@In_(2)S_(3)-rGO纳米棒光电极在0 V(相对于可逆氢电极)的外加偏压下,光电流密度可达1.169 m A cm^(-2),约是Sb_(2)Se_(3)@In_(2)S_(3)和单体Sb_(2)Se_(3)的2倍和16倍,且稳定性良好,在中性条件下平均产氢速率为16.59μmol cm^(-2)h^(-1).实验结果和理论计算均表明,Ⅱ型异质结电荷传输方式是其光电化学增强的物理机制.以上工作为设计基于rGO修饰的复合光电极用于光电化学领域的研究提供了崭新的思路.

摘要：随着电力市场化改革的逐步推进,水电富集区燃煤机组功能定位的转变引发的成本搁浅问题逐渐显现,亟需配置合理的容量成本回收机制。该文通过对燃煤机组容量补偿机制建设的必要性进行分析,设计了符合四川电力市场特性的燃煤机组容量补偿机制,对容量确定方式、成本核算、补偿方式等进行研究,通过重构电价体系阐述了“容量电价+电量电价”的设计原理,并探讨了新电价体系未来发展方向,可为解决四川及国内具有类似燃煤机组容量成本回收问题的省份提供参考。

摘要：为了研究农用全地形车的综合控制策略和无级变速器调速控制系统,首先搭建了农用全地形车动力系统的简化结构,并介绍了无级传送结构原理,实现了无级变速器调速控制策略。仿真结果表明:系统的调节参数可以使车速满足平顺性的要求,且速比的跟随性也比较好。系统具有稳定的动力性和平顺性,符合设计要求。