摘要：A novel Cu?6.5Ni?1Al?1Si?0.15Mg?0.15Ce alloy with super-high strength was designed and its corrosion behavior in3.5%NaCl solution at25°C was investigated by the means of SEM observation,TEM observation and XPS *** alloy after solution treatment,80%cold rolling and aging at450°C for1h had the best comprehensive properties with hardness of HV314,electrical conductivity of19.4%IACS,tensile strength of1017MPa,and average annual corrosion rate of0.028mm/*** oxides and chloride products formed at first,followed by the formation of dyroxides *** alloy showed super-high strength,good electrical conductivity and corrosion resistant because Ni2Si hindered the precipitation of large NiAl at the grain boundary and the denickelefication of the alloy.

摘要：在分析大语言模型特征的基础上,阐述了大语言模型的技术进展与应用领域,认为大语言模型在模型设计、数据结构、预训练和微调方面进步显著,展示了卓越的语言生成、知识运用和复杂逻辑推理等特性,这些特性使其在构建专业模型、提升知识整合和梳理水平、数据挖掘和分析、智能设计与操作领域展现出极大的应用潜力和实用价值。然而,目前模型在可解释性、安全性、真实性及训练成本等方面仍存在诸多挑战。随着算法和结构的优化,模型将实现更高效、更精确的训练,文本学习与生成性能将进一步增强,应用范围将拓展到多模态领域,实现多种类型数据的综合理解与处理。

摘要：设计并制备一种超高强导电Cu-6.0Ni-1.0Si-0.5Al-0.15Mg-0.1Cr（质量分数,%）合金。通过测量合金的硬度,分析经固溶处理并分别经600~850℃等温处理后再在450℃时效处理1 h的合金力学性能的变化规律,建立合金的时间-温度-性能（TTP）曲线。通过透射电镜观察,研究合金在等温处理过程中的第二相的析出规律。结果表明：合金的鼻尖温度约为725℃,淬火敏感区域为675~775℃。合金在淬火敏感区进行等温处理时,晶内析出的δ-Ni_2Si和Ni_3Al迅速形核和长大;延长等温时间,析出相粗化,合金的硬度随之降低。合金在鼻尖温度附近表现出高的淬火敏感性。

摘要：设计并制备Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce(wt.%)合金。采用光学显微镜(OM)、扫描电镜(SEM)、能谱分析和透射电镜(TEM)等测试手段研究合金形变热处理过程中微观组织及性能的变化。合金铸态组织为典型的枝晶组织,铸锭经过920℃热轧后,枝晶组织显著消除。合金的适宜固溶处理制度为960℃/4 h。该合金固溶处理后的冷变形对合金最终性能有很大影响。冷变形程度越大,合金达到硬度峰值的时间越短,硬度峰值和电导率越高。时效温度越高,时效析出过程越快。960℃固溶4 h后冷轧50%,450℃时效2 h硬度峰值可达300.8 HV,电导率20.6%IACS,抗拉强度963.9 MPa,屈服强度950.1 MPa。合金在时效过程中析出纳米级粒子为δ-Ni2Si,其与基体的位相关系为:Cuδ[001][001],Cuδ(110)(010),Cuδ(1 10)(100)。

摘要：基于TRIZ理论,确定一对技术矛盾,选用局部质量原理,设计出带补片的膜片联轴器。利用SolidWorks软件建模,CosmosWorks软件对传统膜片组和带补片膜片组进行了分析。结论是,在同样工况下,带补片膜片组结构比传统膜片组结构降低了应力幅值,提高了抗疲劳能力。