摘要：Basalt fibers/7075 aluminum matrix composites were studied to meet the demand of aluminum alloy drill pipes for material wear *** composites with different basalt fiber additions were prepared by hot pressed sintering and hot *** mechanical properties as well as friction and wear properties of the composites were studied by microstructure analysis,tensile experiments,friction and wear *** results showed that basalt fibers were oriented and uniformly distributed and led to local grain refinement in the alloy *** hardness and elongation of the composites were *** friction coefficient of the composites increased and then decreased,and the maximum wear depth and wear amount decreased,then increased,then decreased again with the growth of basalt fiber ***,the inclusion of basalt fibers mitigated the uneven wear of the extruded 7075 aluminum *** value of wear depth difference of 7075-0.2BF was the smallest,and that of 7075-2.0BF was close to *** maximum wear depth and wear volume the 7075-0.2BF and 7075-2.0BF were also the *** inhibition of uneven wear by basalt fibers enhanced of wear resistance for 7075 aluminum alloy,which has reference significance for improving the performance of aluminum alloy drill pipes.

摘要：随着风力发电技术的快速发展,高性能的电源变换技术受到人们的广泛关注。在此采用基于DSP的数字控制技术,设计了一个新型的AC/DC/AC电源变换器。该变换器前级为三相两开关Boost PFC电路,采用DSP产生两路相位差为180°频率可变的PWM信号进行控制,实现了部分解耦控制,能有效减少输入电流的谐波含量并提高功率因数;后级为三相PWM电压源型逆变电路,采用DSP实现不对称规则采样法完成三相SPWM,输出电压波形接近正弦且减小了谐波电流。在此基础上,进行相关实验,并对结果进行分析。

摘要：将耦合仿生理论应用到孕镶金刚石石油钻头切削齿的结构设计中,从仿生非光滑结构、材料和钻头整体结构3种主要影响因素入手,采用无压浸渍法、热压法和镶焊法等烧制方法和工艺,研制了新型三元耦合仿生孕镶金刚石石油钻头(简称仿生石油钻头),并在普光D-103井须家河组层段进行现场钻进试验。试验结果表明:仿生石油钻头与在须家河层段发挥平稳的三牙轮钻头相比,钻进速度更高、使用寿命更长、整体性能更稳定。

摘要：介绍了采用空气潜孔锤及纵向割缝型UPVC井管技术施工云南楚雄"科技抗旱井"工程,重点阐述了气动潜孔锤钻进技术在坚硬破碎基岩地区水文水井工程中的技术难点、钻进工艺及成井工艺。针对钻进过程中出现的问题,提出钻具改进措施,取得了显著的实钻效果。该工程采用潜孔锤钻进技术提高了钻进效率,减少了工程造价,水井的出水量、水质等各项指标均达到设计要求,获得了良好的经济及社会效益。

摘要：常规素水泥浆封孔材料不能完全满足涌水含气特殊地层条件的封孔要求。以水泥砂浆为研究对象,通过正交实验,设计了水泥砂浆的配比,得到了适用于涌水含气地层的封孔材料配方,达到了钻探对封孔质量的技术要求。在室内实验的基础上,结合通地1井具体地层条件,根据不同井段的封孔质量要求,采用相应封孔材料配方进行了野外应用试验。结果表明,所设计的封孔材料配方能够满足涌水含气地层的封孔质量要求。

摘要：基于仿生耦合理论研制的仿生耦合孕镶金刚石钻头,在工作过程中,仿生单元的提前磨损,会在其底唇面上形成一定的非光滑表面形态,因此其具有钻进效率高和使用寿命长的优点。探讨了仿生单元的同心圆排列方式,即通过改变仿生单元之间的径向和周向距离,来形成一系列非光滑表面形态,然后加工相应的仿生耦合钻头,并进行室内钻进实验,结果表明,径向距离为1.5d(d为仿生单元直径)、周向距离为3.0d和径向距离为2.0d、周向距离为3.5d两种排列方式更能体现仿生耦合钻头高效率、长寿命的优点,相对普通钻头,其效率和寿命分别提高16%、100%和15%、125%。为以后仿生钻头的设计提供了重要依据。

摘要：针对单锁臂结构的控制器设计问题,提出了一种双层同步优化策略,在优化控制器结构的同时设计零极点取值。该方法引入延迟裕度作为后验条件,确保系统在航天器轨道周期内的稳定性,结合控制系统的绝对稳定性和相对稳定性约束,建立控制器结构优化层和参数优化层之间的反馈循环,借助非线性优化算法同步优化控制器结构及参数,在仅需20 dB增益的情况下实现了较高的激光频率噪声抑制比。结果表明,所设计的控制器可使激光频率噪声在0.01 Hz~0.1 mHz频段被抑制5到6个数量级,在0.01 Hz~1 Hz频段被抑制2到3个数量级,满足引力波探测的噪声抑制需求。

摘要：为提高低功耗条件下运放电路的工作速度,基于Class-AB复合型差分对、非线性电流镜传输、交叉耦合对管正反馈3种结构的有机组合,提出了一种高速运算跨导放大电路(OTA)的结构设计方案.该方案在低功耗条件下,电路具有优异的摆率倍增性能,同时电路小信号带宽与低频增益得到一定程度的改善.电路采用CSMC 0.5μm CMOS工艺进行设计并完成MPW流片.在5 V电源电压下测试得到的电路静态功耗仅为11.2μA,最大上升沿与下降沿摆率分别为10和2 V/μs,低频增益60 dB以上,单位增益带宽达到3 MHz.结果表明,新型Class-AB OTA电路比同类参考OTA电路具有更高的大信号瞬态响应品质因子.

摘要：为准确评估矩形钢管混凝土组合桁梁桥节点疲劳性能,引入热点应力法,可通过平面杆系模型、空间杆系模型和三维实体模型计算节点焊趾处的热点应力幅,并通过对52个节点疲劳试验数据回归分析,拟合得到热点应力幅-循环次数曲线;选取陕西黄延高速一座矩形钢管混凝土组合桁梁桥为典型案例进行节点疲劳评估,并对原有节点设计方案的构造进行优化。研究结果表明:相比于墩顶矩形钢管混凝土节点,跨中矩形钢管节点热点应力幅更大,为60.1 MPa,发生在主管表面,但是小于欧洲规范Eurcode中的容许疲劳强度71 MPa,满足疲劳设计要求;对跨中疲劳易损节点进行设计构造优化,原设计矩形钢管节点变为矩形钢管混凝土节点后,管内混凝土改变了节点局部刚度,使相贯线焊趾处应力分布均匀,支、主管表面热点应力幅平均降低25.1%,对原设计节点进行焊缝后处理,可有效消除焊接初始拉应力,改善节点疲劳性能,支、主管表面热点应力幅平均降低14.9%;采用空间杆系模型对优化后的跨中矩形钢管混凝土节点进行疲劳评估,支、主管表面最大热点应力幅分别为58.9、54.1 MPa,大于三维实体模型计算得到的支管和主管表面最大热点应力幅45.2、47.1 MPa,空间杆系模型计算结果偏保守,且无法像三维实体模型一样准确计算不同热点位置的疲劳效应,也无法准确判断疲劳开裂起始位置。

摘要：为了准确确定油藏平面各向异性,避免烦琐的压力图版拟合,提出了基于Tiab直接计算(TDS)技术确定最大、最小方向渗透率及其方位角以及平均平面渗透率和渗透率各向异性度的方法。首先作出平面各向异性油藏干扰试井压力和压力导数双对数曲线,根据曲线交点处的压力和压力导数以及无因次时间,求得激动井观察井的方向渗透率,然后把该方向渗透率代入观察井的各向异性渗透率定量计算模型求解即可。该方法所得结果与现场试验分析测得结果吻合较好。