摘要：The thermal expansion coefficient(TEC)and thermal conductivity(k)of thermal fillers are key factors for designing thermal management and thermal protection composite *** to its unique advantages,hexagonal boron nitride(h-BN)is one of the most commonly used thermal ***,its TEC and k values are still unclear due to the inconsistency of characterization techniques and sample *** this work,these disputes were addressed using the quasi-harmonic approximation(QHA)method and phonon Boltzmann transport equation(BTE)theory based on the density functional theory(DFT),*** accuracy of our calculated TEC and k values was confirmed by previously reported experimental results,and the underlying physical principles were analyzed from the phonon *** TEC results show that the h-BN has small in-plane negative value and large cross-plane positive value,which are-2.4×10^(-6) and 36.4×10^(-6) K^(-1) at 300 K,*** the anisotropic TEC is mainly determined by the anisotropic isothermal bulk modulus and the low-frequency out-of-plane longitudinal phonon *** found that the convergence of cutoff radius and q-grid size have significant effect on the accuracy of k of *** results show that the in-plane k is much higher than the cross-plane k,and the values at 300 K are 286.6 and 2.7 W m^(-1) K^(-1),*** anisotropic phonon group velocity arising from the vibration behaviors of acoustic phonon modes should be primarily responsible for the anisotropic *** calculated TEC and k values will provide important references for the design of h-BN composite materials.

摘要：研究了P/Al比、Cr/Al比对石英纤维增强磷酸盐复合材料物相组成、组织结构、力学性能与介电性能的影响。结果表明,磷酸盐基体的物相组成主要为Berlinite相、低温方石英型AlPO_(4)及未反应的α-Al_(2)O_(3),基体相的组成比例及微观结构受P/Al比、Cr/P比影响较大。当P/Al=4.1、Cr/P=0.04时,复合材料力学性能最佳,拉伸强度为108.6 MPa,弯曲强度为135.3 MPa,断裂韧性K_(IC)为6.6 MPa·m^(1/2),复合材料表现为弱结合界面的塑性断裂特征。分析认为,此时基体中含有较多粘接性能良好的Al(H_(2)PO_(4))_(3)相,基体表现为光滑平面状结构,有利于基体与纤维形成完整连续的良好界面层。此外,材料介电性能受Cr含量影响较大,除Cr/P=0.08材料外,所制备材料介电性能均可满足高温透波材料性能要求,拥有广阔的应用前景。

摘要：改变了碟簧的淬火捆绑方式,由叠放方式改为间隔捆绑方式。淬火、回火后的碟簧放入自行设计的工装中进行了校正。通过改变原有淬火捆绑方式,并增加校正处理工序,使得碟形弹簧的合格率由之前20%提高到90%以上。

摘要：网络协议分析是网络安全及网络监管等应用中的一种关键技术,当前主要是根据已知公开的协议规则以及协议消息数据包格式对协议进行分析。而对于未公开协议的分析技术的研究,有了一些新的进展,但还不成熟。结合现有协议分析技术的优点及特长,设计一种既能分析公开的协议又能分析未知协议的准确、高效的协议分析模型。

摘要：为了分析3D打印碳纤维增强聚醚醚酮(C-PEEK)复合材料的力学行为,探索最优工艺参数进行仿生结构设计,研究了碳纤维含量、打印喷头温度、平台温度、切片层厚度、打印速度、填充度、填充直线角度、填充形状、热处理温度及保温时间等多个工艺参数下,3D打印C-PEEK的力学性能演化规律。结果表明:含10 wt.%碳纤维的C-PEEK拉伸性能最好,并且最佳的3D打印参数为:打印喷头温度440℃、平台温度130℃、切片厚度0.2mm、填充度100%、90°直线填充、打印速度40mm/s、保温腔90℃。此外,根据最佳3D打印参数设计兼具蜂窝多孔和Bouligand旋转夹层的仿生结构,开展抗压强度测试并进行压溃行为分析,发现当层间旋角为30°时对应的蜂窝-Bouligand仿生结构的抗压强度可达24.1 MPa,且具有优异的非灾难性断裂特征。

摘要：非晶SiBCN陶瓷是一类独特的结构材料,具有低比重、高比强度、优异的高温损伤容限等特殊结构和性能,因此在高温防热结构部件上极具应用潜力。通过合理的结构与化学成分协同设计,可探索陶瓷形貌/微观结构演化及断裂行为的基本特征,从而进一步提高其力学性能,以满足实际应用需求。因此,文章以石墨、六方氮化硼、立方硅和硼等元素粉末为原料,提出了采用机械合金化结合高压烧结技术(1 000°C/3~5 GPa/30 min)制备致密非晶Si2ByC2N(y=1.5~4)块体陶瓷的方法。通过XRD、SEM、TEM、TG等表征手段,研究了烧结压力诱导该系非晶陶瓷的组织结构演化、相变及热稳定性,并对其力学性能,特别是断裂行为进行了详细讨论。结果表明,提高烧结压力促使陶瓷基体由完全非晶态向晶态转变,部分块体陶瓷由大量非晶相、少量c-Si和/或t-BN(C)纳米晶相组成,显示出依赖于硼含量的物相组成。高压烧结有效地促进了陶瓷的烧结致密化,导致材料内自由体积的湮灭和"河流状"断裂形貌的产生。随着烧结压力的提高,陶瓷材料的体积密度、纳米硬度和杨氏模量单调增加。在相同烧结条件下,硼含量的增加削弱了非晶Si2ByC2N(y=1.5~4)块体陶瓷的力学性能和热稳定性。1 000°C/5 GPa/30 min烧结制备的致密非晶Si2B1.5C2N块体陶瓷的体积密度、纳米硬度和杨氏模量分别为2.69 g/cm3、33.6±2.2GPa和414.2±16.5 GPa。

摘要：为高效开发利用低品位风能和洋流能,采用涡扇发动机喷管引射技术,设计含有单级涡轮和波瓣引射器结构的低品位风力/洋流涡轮,给出一种波瓣引射器的参数化方法,并基于CFX软件RANS方程和k-ε湍流模型数值研究涡轮气动和引射特性.结果表明：含单级涡轮和波瓣引射器结构的低品位风力/洋流涡轮可将其转子四周流过的能量通过波瓣引射器引入涡轮后侧,通过流向涡和正交涡共同产生的抽吸作用,降低涡轮转子后侧被压,使有效做功速度增大约1.4倍,等效于提升了能量的品位.在2~6 m/s的风能和2~4 m/s的洋流能利用方面,含单级涡轮和波瓣引射器结构的风力/洋流涡轮功率曲线与来流速度成指数增长,流通能力增大32.70%~35.33%,在低速工况能量利用率可达66%~77%.

摘要：为保证西成铁路高地应力节理发育软岩大变形隧道安全修建,采用现场勘察、室内试验、地应力测试、工程类比、数值模拟等方法展开研究,结果表明,西成铁路与毗邻兰渝线地质条件类似,均以二叠系、三叠系板岩与砂岩为主,层理清晰、节理裂隙发育,地应力以水平主应力为主导,水平主应力在10~30 MPa之间,竖直主应力在4~13 MPa之间,有较强水平构造应力作用,兰渝线控制围岩变形主要采用增加预留变形量、自进式长锚杆、钢花管加固、增加初支及衬砌刚度、钢纤维喷射混凝土等技术措施。在此基础上针对西成铁路节理发育软岩大变形主要发生在垂直节理倾角方向上的特点,提出首先增大矢跨比,然后增大钢拱架刚度,对于Ⅲ级大变形在垂直节理方向设置预应力锚索的非对称大变形隧道支护体系,该支护体系相比传统支护体系能够减小13.8%~21.2%软岩变形,对于控制节理发育软岩变形效果良好。

摘要：通过扩展数字盆地的三维引擎接口,将数字盆地直连VR头显,主要包括VR头显直连方式研究、交互动作的设计和实现、VR效率和效果的优化等内容。影响VR应用的主要因素是内容制作和分发平台,而胜利油田济阳坳陷数字盆地系统管理着诸多勘探数据模型并提供了三维可视化能力,正好可以作为虚拟现实应用中的内容提供者和内容分发平台,并且是动态的,只要被纳入在数字盆地系统管理下的数据均可以在虚拟现实环境中被显示和观察。通过开展基于数字盆地的虚拟现实研究,使济阳坳陷数字盆地能够以虚拟现实的方式被观察和研究。

摘要：为提高军事理论相关课程教学质量,针对军事历史、军事思想、军事战略3门生长军官本科必修课程教学目标相近性、教学内容相通性、教学方法手段相似性的特点,从上述3个方面进行一体化教学设计,制订三课融合教学计划,实施三年一贯制衔接教学,改进教学方式方法,总结教学中应重点注意的制定合理目标、做好交叉衔接、详略安排得当等问题,有效提升学员军事理论素养。