摘要：The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were *** CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solution *** contrast,nanocrystalline HfNi_(3) anchoring in amorphous structures is found in the(CoCrFeNiMn)_(90)Hf_(10) ***(CoCrFeNiMn)_(90)Al_(10) powders show better ferromagnetic behaviors,mainly explained by the facilitated motion of the magnetic domain induced by the coherent interface between duplex *** with our previous work,the rules of forming solid-solution and amorphous phase in as-milled HEA powders are preliminarily *** is found that,compared with the as-cast HEA reported previously,the variation range of mixing enthalpy with atomic size difference of the solid-solution formed in as-milled HEA powders is ***,the variation ranges between mixing enthalpy and entropy with atomic size difference of the amorphous phase in HEA powder become wider than those of high-entropy bulk metallic glass.

摘要：《吕氏乡约》应溯源至南方少数民族的"款"。《吕氏乡约》是因应土地私有和人口流动、宗族重整、乡村"官治"不足、政治改革无力等多问题的理学探索和设计。乡约的自治性质和教化功能,是有限的自治性和实质的他治性之间充满张力的结合。乡约的效力应从国家的、伦理的、事实的和心理的维度加以实证研究,以确证乡约的制度性而非观念性事实存在。

摘要：以某流域水环境综合整治项目的智慧水务系统设计为例,介绍了系统架构及其在污水管网中的应用。针对污水管网覆盖范围广、故障排查困难、运维工作量大的特点,通过构建污水管网GIS系统,实现排水设施的“一张图”可视化管理,通过在管网中设置管道水位、水质、流量、雨量等仪表,实现排水系统在线监测和动态实时感知,从而及时发现偷排、外水入侵、管网堵塞等故障,降低运维工作量。

摘要：为摸清南京市主城区海绵空间特征,选取9个表征洪涝韧性、蓝绿灰海绵空间特征的指标构建了“压力—状态—响应”(Pressure-State-Response,PSR)评价模型,对南京市主城区海绵空间特征进行评价。结果表明,南京市主城区低韧性、中韧性、高韧性排水分区比例为45.95∶24.32∶29.73;建成率较高的区域,受用地限制,水系连通性、绿色空间格局等状态层指标得分较低;而建成率稍低的区域,水系连通性、绿色空间格局、排涝能力等状态层指标与响应层指标对洪涝韧性均有较大影响。根据PSR模型结果,南京市主城区可通过蓝绿灰海绵空间的进一步统筹建设提升区域洪涝韧性。

摘要：A medium wave(MW)640×512(25μm)Mercury Cadmium Telluride(HgCdTe)polarimetric focal plane array(FPA)was *** micro-polarizer array(MPA)has been carefully designed in terms of line grating structure optimization and crosstalk suppression.A monolithic fabrication process with low damage was explored,which was verified to be compatible well with HgCdTe *** monolithic integration of MPA,NETD<9.5 mK was still ***,to figure out the underlying mechanism that dominat⁃ed the extinction ratio(ER),specialized MPA layouts were designed,and the crosstalk was experimentally vali⁃dated as the major source that impacted *** expanding opaque regions at pixel edges to 4μm,crosstalk rates from adjacent pixels could be effectively reduced to approximately 2%,and promising ERs ranging from 17.32 to 27.41 were implemented.

摘要：普通四线制铂电阻测温系统受恒流源长短期漂移、导线热电动势影响,其测量准确度难以超过0.1℃量级。本文分析了一种改进型4线制高精度铂电阻测温方法的原理误差,并设计了相应的高精度铂电阻测温系统。采用温度系数小、阻值稳定性好的参考电阻作为铂电阻阻值测量基准,消除了恒流源长期漂移引起的铂电阻测温误差;分别在正、反向恒流激励条件下测量了铂电阻上的电压,利用导线热电势大小与方向的短期不变性,对得到的两电压量求差以消除导线热电势的影响;通过半导体致冷器(TEC)控制恒流源温度来减小恒流源的短期电流漂移,进而减小其对铂电阻测温精度的影响;设计了精度高、阶跃响应速度快的分时复用式电压信号采集单元用来高精度地测量铂电阻和参考电阻上电压量的比值。等效实验和校准实验结果表明,高精度铂电阻测温系统的测量稳定性优于0.005℃/10day,测量分辨力优于0.005℃,测量准确度为0.02℃(k=2),满足超精密激光干涉测量系统提出的高精度温度测量需求。

摘要：为协调和共享制造网格中分布的资源,设计并实现了一个面向网格服务的任务管理系统。建立了该系统的功能模型和工作流程,定义了面向零件和组件加工任务的网格资源节点模型和任务模型;基于任务时间、成本和服务质量的约束,建立了任务分解规则和资源节点的匹配规则,设计了任务调度及状态监控方案;最后构建了系统实现的体系结构和信息交换过程。基于网格原理,系统各功能被封装为网格服务,通过任务管理中心实现对服务的调用。系统已被集成到某区域网络化制造服务平台,为企业提供了与制造过程相关的网格服务。

摘要：针对传统幂次趋近律存在的抖振以及全局收敛缓慢的问题,提出一种新型复合滑模趋近律,该趋近律通过引入正切函数以及对传统幂次趋近律的改进,实现趋近律的快速收敛和无抖振特性.首先,引入正切函数,在初始状态已知的情况下使系统更快地收敛;其次,通过设计的趋近律改进传统幂次趋近律中含符号函数乘积项容易引起的抖振;然后,理论证明新型复合趋近律能够快速收敛且无抖振,并推导出趋近速率及稳态误差界;最后,以直线磁悬浮同步电动机磁悬浮系统为例,与双幂次趋近律和多幂次趋近律仿真对比,进一步验证新型复合趋近律能够明显缩短系统的动态过程并消除抖振,且存在模型不确定性及外加干扰作用下,系统仍能迅速地收敛到平衡点附近的领域内.

摘要：针对目标信号源波达方向(DOA)的实时变化,将人工蜂群算法应用于最大似然函数的优化,实现了动态目标DOA的实时跟踪。首先,提出了一种可变遗忘因子的自适应样本协方差矩阵更新方法,该方法可根据目标信号源DOA变化的快慢自适应调整历史数据和当前采样数据在协方差矩阵中所占的权重,从而保证在获得较小稳态误差的同时又可获得较快的跟踪速度。然后,直接应用了性能优越的最大似然估计方法,避免了子空间跟踪类算法需要不断重复特征值或奇异值分解等问题。最后,采用人工蜂群仿生智能算法对似然函数的求解进行优化,从而极大地减少了算法的计算量,保证了算法的快速性和实时性。实验结果表明:在单快拍采样的情况下,信噪比为0dB时,跟踪两个目标信号源的均方根误差为0.995 2°,基本达到了阵列信号处理中目标跟踪方法的设计要求。

摘要：对所研究的熔模型薄壁特征件真空吸铸工艺过程中的浇注系统及排气系统进行了设计,并利用数值模拟软件对薄壁件的充型过程和可能产生的铸造缺陷进行了仿真模拟。结果表明:真空吸铸成形方法能够较好地解决浇注该铸件时易遇到的充型困难、喷溅及憋气等技术难题,可获得轮廓完整、内外品质优良的合格精铸件;立式单通道浇注方案优于卧式双通道浇注方案,使合金液流充型过程平缓顺畅,能够避免金属液出现汇流和冲击现象,减少铸造缺陷的产生。