摘要：Climate change caused by the increasing emission of CO_(2)to the atmosphere has become a global *** ameliorate this issue,converting CO_(2)into valuable chemicals is highly desirable,enabling a sustainable low-carbon *** this end,developing efficient catalytic systems for CO_(2)conversion has sparked intense interests from both academia and *** advantage of their highly porous structures and unique properties,metal−organic frameworks(MOFs)have shown great potential as heterogeneous catalysts for CO_(2)*** transformations involving CO_(2)have been accomplished over MOFs-based *** we provide a comprehensive and up-to-date review on recent advances of heterogeneous CO_(2)thermocatalysis using MOFs,highlighting relationships between structures and *** attention is given to the design strategies for improving the catalytic performance of *** available to enrich the catalytic active sites in MOF structures are stressed and their respective impacts on CO_(2)conversion efficiency are *** synergistic effects between each active site within the structure of MOFs and derivatives are *** the end,future perspectives and challenges in CO_(2)conversion by heterogeneous catalysis with MOFs are described.

摘要：为了提升微结构注塑机的成型精度,提高合模系统的合模力稳定性和运动特性尤为重要。文章设计了由伺服电机驱动的1300 k N微结构注塑机的合模系统。在此基础上,建立了该系统的三维几何模型,并在Adams虚拟样机环境中对开合模过程进行了多体系统动力学及运动学仿真。仿真结果表明,在移模速度600 mm/s时,合模系统的开合模运动保持相对平稳。这对于保证制品质量和提高成型加工效率具有重要意义。此研究为提高微结构注塑机合模系统的设计精度和成型质量提供了理论依据。

摘要：水系锌离子电池(AZIBs)作为一种低成本、高安全的新兴且前景广阔的储能技术近年来备受关注。新型MXenes材料由于其独特的结构特征和物理化学性质,如易调节的二维结构、优异的导电性、化学组成多样和可控的表面化学特性,在AZIBs中表现出独特的应用优势。本文全面综述近年来MXenes在AZIBs中应用的研究进展,探讨MXenes应用于AZIBs正负极的结构设计及性能优化策略:在正极方面,MXenes可直接作为活性物质或活性物质前驱体、基体材料,以获得高活性、优异的循环寿命和倍率性能;在负极方面,MXenes可作为锌沉积的二维/三维载体、亲锌基体及锌金属界面保护层,以减缓电化学反应过程中锌金属的腐蚀和枝晶生长。此外,本文也对MXenes基材料在AZIBs中应用的发展方向进行展望。

摘要：采用田口方法对聚芳硫醚砜/玻纤布复合材料的浸渍工艺进行了优化。按照田口直交矩阵设计的参数组合进行制样并进行力学测试,测试结果以方差分析进行统计分析。表明最佳浸渍工艺为浸渍温度170℃,浸渍压力330Pa,浸渍时间7 min,此工艺条件下复合材料的拉伸强度为284 MPa。

摘要：采用原位溶剂热生长法设计合成了锌掺杂Co9S8纳米颗粒。各种表征技术和性能测试结果表明:锌掺杂Co9S8纳米颗粒的孔尺寸为18 nm,比表面积为23 m^2·g^-1;同时微量的锌掺杂显著增强了Co9S8的电催化析氢(HER)活性及电容器性能。在HER性能测试中,当电流密度为10 mA·cm^-2时电位为-361 mV,电流密度最高可达38.26 mA·cm^-2,且具有优异的循环稳定性。同时在电容器性能测试中具有较高的比电容,当电流密度为1 A·g^-1时,质量比电容和面积比电容分别为235.48 F·g^-1和812.4 mF·cm^-2。

摘要：沸石咪唑骨架材料(zeolitic imidazolate frameworks, ZIFs)因其大比表面积、规则孔道结构、骨架可调控、水热稳定性等特点,在吸附、分离和催化领域具有广阔的应用前景.本工作基于模板法设计和制备双"T"型连续液滴式微流控芯片,通过多相持续进料,稳定快速合成单斜晶C2/cZIF-7(方纳石结构),ZIF-8和Co-ZIF-8等材料,从而减少产物的差异性.微流控芯片连续制备得到的ZIFs具有非常高的结晶度和均一性.此外,通过调节起始反应物浓度和停留时间,实现了ZIFs产物粒径和形貌的调控.微流控芯片提供了一种简易可控快速宏量制备ZIFs材料的新方法.

摘要：基于柱壳和拉普拉斯薄膜理论的筒身和封头应力场计算会导致赤道圆处径向位移不协调,出现理论上的结构分离现象,与结构整体承载过程中实际变形不符。针对纤维缠绕复合材料壳体封头变角度、变厚度、变曲率现象导致应力分析困难问题,以该变形不协调为切入点,开展纤维缠绕复合材料封头复杂应力场有矩理论分析,综合考虑赤道圆处存在的几何突变和材料刚度突变结构因素,并等效处理金属接头端面内压载荷为该接触部分复材的等效内压载荷,得到等效后的径向薄膜位移作为控制方程极孔边界条件,构建了基于板壳理论和宏观层合板理论的纤维缠绕复合材料壳体一体化有矩模型,基于该模型探究了极孔附近胀口现象形成机理。进行了?150干法缠绕标准试验壳体打压实验,该理论方法计算结果与实验测试结果对比表明,该方法具有较高的计算精度,结合该理论计算结果,从结构、材料刚度突变方面探究了纤维缠绕壳体封头力学响应复杂的内部机理,以及不同缠绕方案下壳体应力的变化规律。该研究成果可以为纤维缠绕复合材料壳体结构设计提供理论支撑,对设计之初快速了解壳体整体应变状态具有重要意义。

摘要：日益流行的柔性电子器件要求在反复变形状态下,材料仍能保持优异的力学和电学性能.而石墨烯作为一种二维(two dimensional,2D)碳纳米片,具有独特的力学和电学性能,成为构筑此类柔性电子器件的首选基元材料.然而,如何将石墨烯纳米片组装成高性能的石墨烯纳米复合材料,仍然存在巨大挑战.天然鲍鱼壳因其内部有序规整的层状结构和丰富的界面相互作用,而具有综合优异的力学性能.这种独特的界面结构设计,为2D纳米片仿生组装提供了新的思想源泉.本文按照"有所发现,有所发明,有所创造"的学术研究思路,总结了最近几年国内外课题组关于仿生石墨烯纳米复合材料(bioinspired graphene-based nanocomposites,BGBNs)的研究进展;分析了石墨烯层间不同的界面相互作用;详细讨论了基于协同效应,仿生构筑强韧一体化石墨烯纳米复合材料的策略;重点阐述了BGBNs的拉伸强度、韧性以及电导率等基本物理性能.最后,本文也简单概括了BGBNs在柔性电子器件领域的应用和潜在的挑战,并展望了BGBNs未来的发展方向.

摘要：自然界中,鲍鱼壳具有有机-无机多级次层状结构以及大量的复合界面作用,力学性能优异。这一独特的层状结构主要由霰石碳酸钙片层构成,并通过体积分数约为5%的生物高分子在层间进行粘合。受鲍鱼壳这一微观结构的启发,我们利用不同的基元材料如纳米蒙脱土、碳纳米管以及氧化石墨烯等构筑仿鲍鱼壳层状结构,并结合多种界面设计,实现不同界面、不同基元材料之间的协同作用,得到了力学性能优异的高分子纳米复合材料。仿生高分子纳米复合材料的成功制备,为今后的研究提供了崭新的思路,拓宽了高分子纳米复合材料的应用前景。