摘要：Thin-walled aluminum alloy tube numerical control （NC） bending with small bending radius is a complex process with multi-factor coupling effects and multi-die constraints. A significance-based optimization method of the parameters was proposed based on the finite element （FE） simulation, and the significance analysis of the processing parameters on the forming quality in terms of the maximum wall thinning ratio and the maximum cross section distortion degree was implemented using the fractional factorial design. The optimum value of the significant parameter, the clearance between the tube and the wiper die, was obtained, and the values of the other parameters, including the friction coefficients and the clearances between the tube and the dies, the mandrel extension length and the boost velocity were estimated. The results are applied to aluminum alloy tube NC bending d50 mm×1 mm×75 mm and d70 mm×1.5 mm×105 mm （initial tube outside diameter D0 × initial tube wall thickness t0 × bending radius R）, and qualified tubes are produced.

摘要：The investigating of the hot press process parameters on the flexural properties of LVL （Laminated Veneer Lumber） reinforced composites derived from rubber wood veneer reinforced with fiber glass woven and epoxy adhesive were performed via the DOE （design of experimental） approach. It was discovered that pressure was the most significantly and negatively effect on the product properties. Enhancing in the mechanical properties was related to decrease the processing pressure. Beside, press time was also significantly and positively effect. Although time was not clearly reflect from the mechanical results, but it was detected from the ANOVA （analysis of variance）results. The mechanical properties were increased with increasing compression time. From the results, the optimal condition to maximize mechanical properties was assumed at low pressure, 15 bars, low temperature, 70℃, and long time, 60 mins. The durability testing including screw nail withdrawal strength, water absorption, and termite resistance of LVL reinforced composite were also studied. The results are shown that the LVL wood has superior properties when compare with solid woods. It was found the withdrawal strength of LVL reinforce composite was higher than the solid woods. As expected that solid woods, except eucalyptus, had low water absorption resistance as it more hygroscopic corresponded to LVL reinforced wood. Also solid woods, except teal（, had low resistance to termite attack. Therefore, LVL reinforced was the best candidate by mean of durability properties compared to solid wood.

摘要：With the recent advancement in nanotechnology,nanoparticles(NPs)offer an ample variety of smart functions than conventional materials in various *** compared to larger particles,NPs possess unique characteristics and excellent abilities,such as low toxicity,chemical stability,surface functionality,and *** advantageous properties allow them to be widely utilized in many applications,including biomedical applications,energy applications,IT applications,and industrial *** order to fulfill the increasing demands of NP applications,existing NP synthesis methods need to be improved based on the requirements of different applications to further their usage.A comprehensive understanding of the relationships between synthesis parameters and properties of NPs can help us better fine-tune them with designed properties and minimal *** review paper will discuss the commonly used synthesis methods of functionalized NPs,as well as future directions and challenges to develop various synthesis methods further.