摘要：The mechanism of oxygen pressure acid leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation was investigated in this *** sphalerite was fabricated with varying amounts of iron content via the sintering of ZnS and FeS and used for the pressure acid leaching *** variations in the potential of the pressure leaching system were investigated by using a self-designed potential *** results showed that compared to the non-iron sphalerite,there was a violent redox reaction between the 25.70%Fe-artificial sphalerite and dissolved oxygen during the process of pressure leaching;and the catalytic mechanism was attributed to the redox couple Fe^3+/Fe^2+,where Fe3+oxidizes the H2S gas film and the reduced Fe2+state is subsequently oxidized by the dissolved ***,the effect of temperature,H2SO4 concentration,and oxygen partial pressure on the artificial sphalerite with different iron contents was *** sphalerite samples with iron content were observed to dissolve more easily in sulfuric acid compared to the non-iron ***,the activation energy of artificial sphalerite was observed to be lower in the sample with 25.70%iron content(22.26 kJ/mol)compared to that with no iron(32.31 kJ/mol);and the apparent reaction orders were obtained with respect to H2SO4 concentration(1.10 and 1.36)and oxygen partial pressure(1.29 and 1.41),respectively.A comprehensive kinetic model was developed on the basis of the experimental data and the fitted leaching ratio plot;and the kinetic equations for the leaching of sphalerite catalyzed by Fe^3+/Fe^2+self-precipitation were determined.