摘要：Zero-dimensional metal halide perovskites have captured intense research interest owing to their unique optoelectronic ***,metal halides with the ns^(2) electronic configuration are of great interest owing to the high-temperature sensitivity of their photoluminescence,which could be applied to remote optical thermometry(ROT).Herein,all-inorganic and lead-free halide perovskite Te^(4+)-doped Cs_(2)InCl_(5)·H_(2)O single crystals(SCs)were prepared through the hydrothermal method and showed a strong temperature dependence of photoluminescence *** Te^(4+) doping,the nonemissive Cs_(2)InCl_(5)·H_(2)O SC exhibits a bright orange emission at 660 nm with a wide full width at half maximum of 180 *** strong phonon-exciton coupling promotes the formation of self-trapped excitons in the soft lattice of the zero-dimensional Te^(4+)-doped Cs_(2)InCl_(5)·H_(2)O *** Te^(4+) ions with the 5 s^(2) electronic configuration endow the Te^(4+)-doped Cs_(2)InCl_(5)·H_(2)O SC with a strong temperaturedependent photoluminescence *** SC reaches a maximum specific sensitivity of 0.062 K^(-1) at 320 K,thereby showing the potential advantages of indium-based metal halide perovskites in ROT applications.

摘要：Both bismuth and copper are non-toxic and earth-abundant elements suitable for lead-free halide perovskite-like photovoltaic devices. Here, we report a highly facile route for in-situ producing copper-bismuth-iodide(CuBiI4) thin films directly on ITO substrate at room temperature, by utilizing a Bi-Cu alloy layer as precursor. X-ray diffraction and transmission electron microscopy(TEM) results verified the formation of well crystallized CuBiI4 thin films with [222] orientation. The transient photovoltage(TPV) analysis revealed that the CuBiI4 is an n-type semiconductor with a suitable band gap of ~1.81 eV, preferable to photoelectric conversion compared with CH3NH3PbI3. It is very interesting that the subsequent spin-coating process of the classical Spiro-MeOTAD organic solution with TBP and acetonitrile resulted in a dense and smooth CuBiI4:SpiroMeOTAD bulk-heterojunction film. The preliminarily fabricated simple sandwich structures of ITO/CuBiI4:Spiro-MeOTAD/Au hybrid solar cell devices displayed efficient photovoltaic performance with the PCE up to 1.119% of the best sample. The room temperature direct metal surface elemental reaction(DMSER) method may provide a new insight for all-inorganic lead free perovskite-like AaBbXx compounds and high performance photovoltaic devices.