摘要：Different treatments were conducted over Ti6Al4V samples in order to produce a surface modification to increase cell attachment and *** surface treatments evaluated in this study were as follows:etching with sulfuric acid/hydrochloric acid,oxidizing with hydrogen peroxide and low-pressure oxygen plasma *** contrast to other works found in the literature,this research conducts a comparison between different chemical and physical treatments in terms of different assays for surface characterization:X-ray diffraction,scanning electron microscope(SEM),energy-dispersive X-ray spectroscopy,water contact angle,release of vanadium ions and cell viability tests(MTT)of human osteoblasts(hFOB 1.19).Cell morphology over the different substrates was also studied by SEM *** was found that plasma and peroxide treatments increase the O/Ti ratio at the titanium surface and provide an increase in cell *** the other hand,acid etching provides a superhydrophilic surface which is not able to improve the cell attachment of human osteoblasts.

摘要：Polycaprolactone-carboxymethyl cellulose composites have been obtained and used to print porous structures by material *** materials used contained 0,2 and 5% w/w of the carboxymethyl cellulose *** structures have been analyzed in terms of their morphology (including the evaluation of their porosity),mechanical properties under compression load and cell *** affinity has been evaluated by culturing sheep mesenchymal stem cells and analyzing their viability by the Alamar Blue(R)assay at days 1,3,6 and *** results show that composites samples have similar values of porosity and apparent density than pure polycaprolactone ***,samples containing 5%w/w of carboxymethyl cellulose have micropores on the filaments due to a hindered deposition *** characteristic affects the mechanical properties of the structures,so these ones have a mean compression modulus significantly lower than pure polycaprolactone ***, the samples containing 2%w/w of carboxymethyl cellulose show no significant difference with the pure polycaprolactone ones in terms of their mechanical ***,the presence of 2%w/w of additive improves cell proliferation on the surface of the porous *** complementary information,the flow properties of the composite materials were studied and the power law equations at 210℃ obtained,as this temperature was the 3D printing *** equations can be useful for simulation and designing purposes of other manufacturing processes.