摘要：Flexible supercapacitors(SCs)have become a popular research topic due to their extra-long service life,foldability,and ***,their low energy density restricts their ***,we synthesized phosphorus-doped bimetallic sulfides embedded in heteroatom-doped(N,S,and P)carbon shells(P-ZCS/HC)using a simple approach to create high-performance flexible *** three-dimensional architecture made by interlaced nanosheets was preserved,and raised nanoparticles appeared on the rough surface during the annealing operation,increasing the specific surface area and potential exposure to the *** is noteworthy that the optimal P-ZCS/HC electrode possessed a remarkable capacity of 1080 C g^(-1)at 1 A g^(-1)along with superb cycling *** extraordinary properties were primarily caused by plentiful redox reactions,enhanced conductivity,and synergic effects of the P-doped metal sulfides and heteroatom-doped carbon *** functional theory simulations confirmed the good function of the P-doped electrodes and their ability to boost conductivity,improve reactive dynamics,and promote ***,the assembled all-solid-state hybrid SC exhibited a maximum energy density of 62.9 W h kg^(-1)and a power density of 16 k W kg^(-1),while being able to maintain 92.0%of its initial capacity after 10,000 *** systematic report provides new insight into the design and synthesis of electrodes with complex components and outstanding structures for the flexible energy field.

摘要：MXene具有丰富的高电负性末端原子、较大的比表面积和较小的原子厚度等优点,已被用作前驱体制备多种纳米材料.然而,目前已报道的用于衍生金属有机框架(MOF)的MXene仅限于V_(2)CT_(x).因此,通过增加MXene和有机配体的种类,合理设计和合成新型MOF,并进一步深入探索其合成机理仍是目前面临的重要挑战.本文采用金属离子辅助转化策略,以二维Ti_(3)C_(2)T_(x)为前驱体,合成了具有非互穿SrSi2(srs)框架的基于儿茶酚的三维(3D)TiCu-HHTP(HHTP=2,3,6,7,10,11-六羟基三苯)MOF.该策略表现出了良好的普适性,Ti3C2和辅助Cu^(2+)离子可以扩展到V2C MXene和其他辅助金属离子Mn^(+)(M=Ni^(2+)、Co^(2+),Mn^(2+)和Zn^(2+)).转化机制包括从Ti3C2纳米片到辅助金属离子的电荷转移、Ti-C键断裂促进释放Ti^(4+)离子以及Ti^(4+)/Mn^(+)与HHTP之间的强螯合配位协同促进TiCu-HHTP的形成.独特的3D导电网络和丰富的氧化还原位点赋予了TiCu-HHTP-7/PPy复合柔性透明电极快速的离子/电子传输和可逆的法拉第反应.在0.02 mA cm^(-2)电流密度下,TiCu-HHTP/PPy透明电极的面积比电容值达到3.63 mF cm^(-2),明显高于纯PPy电极的面积电容值(1.79 mF cm^(-2)).TiCu-HHTP/PPy透明电容器在0.75μW cm^(-2)的功率密度下,能量密度为0.042μWh cm^(-2).