摘要：A type of multi-core Er-doped photosensitive silica optical fiber （MC-EDPF） is proposed and fabricated, in which a high consistency Er-doped core is surrounded by six high consistency Ge-doped cores. The multi-core design can overcome the difficulties encountered in the design and fabrication of single-core EDPFs through a modified chemical vapor deposition method combined with solution doping technology, and there is a conflict between high consistency Er doping and high consistency Ce doping. The absorption of MC-EDPFs achieved 15.876dB/m at 1550mm and lOdB/m at 98Ohm. The refleetivity of the fiber Bragg gratings （FBCs） written directly on the MC-EDPFs is as much as 96.84%.

摘要：A kind of erbium doped photosensitive fiber(EDPF) was proposed and fabricated,whose core was made of double layers named photosensitive layer and erbium doped *** double-layer core de-sign can overcome difficulties in fabrication of EDPF with single core design,*** conflict between the high consistency rare earth doping and high consistency germanium doping.A sample was fabri-cated through the modified chemical vapor deposition method combined with solution doping *** peak absorption coefficient was 48.80 dB/m at 1.53 μm,the background loss was lower than 0.1 dB/m,and the reflectivity of the fiber Brag gratings(FBG) written directly on the sample fiber was up to 97.3% by UV-writing ***,a C band tunable fiber laser was fabricated using the sample fiber,in which a uniform FBG was written directly on EDPFs as a reflector.A single wavelength lasing with a maximum wavelength tuning range of 1555.2―1558.0 nm was achieved *** this tuning range,the full-width at half maximum(FWHM) of the laser output was smaller than 0.015 nm and the side mode suppression ratio(SMSR) was better than 50 dB.