摘要：Phase change materials (PCMs) can be incorporated with low-cost minerals to synthesize composites for thermal energy storage in building *** coal (SC) after vanadium extraction treatment shows potential for secondary utilization in composite *** prepared SC-based composite PCMs with SC as a matrix,stearic acid (SA) as a PCM,and expanded graphite (EG) as an *** combined roasting and acid leaching treatment of raw SC was conducted to understand the effect of vanadium extraction on promoting loading *** showed that the combined treatment of roasting at 900℃ and leaching increased the SC loading of the composite by 6.2%by improving the specific surface *** loading capacity and thermal conductivity of the composite obviously increased by 127%and 48.19%,respectively,due to the contribution of 3wt% *** data were supported by the high load of 66.69%and thermal conductivity of 0.59 W·m^(-1)·K-1of the designed *** obtained composite exhibited a phase change temperature of 52.17℃,melting latent heat of 121.5 J·g^(-1),and good chemical *** SC-based composite has prospects in building applications exploiting the secondary utilization of minerals.

摘要：Aqueous Zn-iodine(Zn-I_(2))batteries have attracted extensive research interest as an emerging redox conversion energy storage system due to the low cost and high ***,the shuttling effects of polyiodides arising from incomplete redox conversion and inhomogeneous Zn plating on the Zn anode surface always hinder the commercial application of Zn-I_(2)*** this work,a two-birds-with-one-stone strategy is reported for long-life Zn-I_(2)*** on the strategy,the sulfonate-functionalized carbon fiber not only acts as the excellent iodine limiter to inhibit iodine species shuttling,but also as the uniform Zn plating guidance layer on the Zn anode surface to prevent the inhomogeneous deposition of Zn^(2+).Consequently,a superior cycling stability(a capacity of 124 mAh g^(-1)after 10,000 cycles at 5 A g^(-1))is *** calculations illustrate that sulfonate groups successfully induce charge redistribution on the carbon substrate,thereby strengthening the electronic interactions of the iodine species with the carbon *** charge-enriched sulfonate groups can guide the uniform deposition of Zn^(2+)through a strong Coulombic effect with Zn^(2+).This work gives a new perspective on the integrated design of cathodes and anodes for rechargeable batteries.